1428 High performance structural bonding acrylic adhesive
Typical Applications
Transport vehicles, notebook computer, mobile phone and other products such as structural adhesive bonding electrons.
Bonding material: ABS, glass steel, polyester (DCPD modified) polystyrene, polyethylene ester, PVC, polyurethane, coating
Carbon steel, aluminum and stainless steel recommended HuiTian primer 1020.
Technical Data
| Item | Unit | Typical Value | ||
| Color | Component A | White | ||
| Component B | Blue | |||
| Component of Basic Materials | acrylic acid | |||
| Density | Component A | g/cm3 | 0.97 | |
| Component B | 1.13 | |||
| Viscosity | Component A | mPa*s | 120000 | |
| Component B | 150000 | |||
| After Mixed | ||||
| Mix Ratio by weight (A:B) | 10:1 | |||
| Handing Curing Time | Min | 6 | ||
| Initial Curing Time | Hour | 0.5 | ||
| Full Curing Time | Hour | 24 | ||
| Tensile Strength | After Curing | Mpa | 20 | |
| Elongation at break | % | |||
| Hardness | Shore A | |||
| Volume Resistivity | Ω*cm | |||
| Dielectric Strength | KV/mm | |||
| Flame Retardant Rating | UL94 V-1 | |||
| Work Temperature | ℃ | -55~121 | ||
Medium resistance
Resistance PH 3-10 acid, hydrocarbons, salt solution. Not resistant to polar solvent, acid and alkali.
Mixing Adhesive:
Through a fixed mixing ratio of the mixing nozzle mix, with manual, pneumatic or equipment gluing
Clean:
Before curing is easier to clean, wipe the lotion, overflow adhesive residue available containing citric acid, terpene resin or NMP degreasing agent scrub in order to achieve the best results. If the layer has been cured, carefully will layer off, and wipe the lotion good cleaning effect.
Matters need attention
1．This product is flammable, away from heat and flame, spark store or use.
2．Not including the adhesive materials: PP, PE, POM, PTFE, copper, brass
3．All stainless steel, aluminum, mixing equipment be Teflon or PE material. Filler, pump shall not use copper or copper alloy. The sealing ring must use Teflon, Teflon coated PVC, PE/PP, VITON, NBR, chloroprene rubber or other elastic body shall not be.
4．This product is curing very fast, generates a lot of heat when mass mixing, and may be accompanied by release of gas, steam and other volatiles. Therefore, should be in every time limited quantity in mixed operation time can run out, and the adhesive thickness is controlled within 3.2mm
Package
50ml/ Double tube, 12 double tube /carton.
Storage
1.Store it in dry and shady places at the temperature of 12~24℃ is best
2.A component Storage life: 12 months,,B component 9months
3. Could not frozen storage